品牌：Sabic
品名：Xenoy
品类：PC/PBT
牌号：5720U
色号：5720U-1001，5720U-4543，5720U-BK1066，5720U-BK1067，5720U-BL2G008，5720U-BL4F021，5720U-BL7G036，5720U-GN2E060，5720U-GN4D164，5720U-GN8E037，5720U-GY2G089，5720U-GY3D636，5720U-GY4F041，5720U-GY6F043，5720U-GY7G045，5720U-GY8G004，5720U-OR2F001，5720U-WH9G046，5720U-YW5E100
中文简介：5720U，未增强PC/PBT合金化聚合物。杰出的低温抗冲击性/耐化学剂性。XENOY 5720的紫外稳定牌号。
XENOY™ 5720U resin
Polycarbonate + PBT
SABIC Innovative Plastics
产品说明：
Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
物性信息：
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.17 |
g/cm³ |
ASTM D792, ISO 1183 |
| 特定体积 |
0.850 |
cm³/g |
ASTM D792 |
| 熔流率（熔体流动速率） |
|
|
|
| 250°C/2.16 kg |
3.8 |
g/10 min |
ASTM D1238, ISO 1133 |
| 250°C/5.0 kg |
11 |
g/10 min |
ASTM D1238, ISO 1133 |
| 265°C/2.16 kg |
6.8 |
g/10 min |
ASTM D1238 |
| 266°C/5.0 kg |
20 |
g/10 min |
ASTM D1238 |
| 溶化体积流率（MVR） |
|
|
ISO 1133 |
| 250°C/2.16 kg |
3.60 |
cm³/10min |
ISO 1133 |
| 250°C/5.0 kg |
10.9 |
cm³/10min |
ISO 1133 |
| 265°C/2.16 kg |
6.50 |
cm³/10min |
ISO 1133 |
| 265°C/5.0 kg |
18.9 |
cm³/10min |
ISO 1133 |
| 收缩率 - 流动 (3.20 mm) |
1.0 到 1.2 |
% |
内部方法 |
| 吸水率 |
|
|
ISO 62 |
| 饱和, 23°C |
0.28 |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
0.080 |
% |
ISO 62 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| -- 1 |
1830 |
MPa |
ASTM D638 |
| -- 2 |
1830 |
MPa |
内部方法 |
| -- 3 |
1820 |
MPa |
ASTM D638 |
| -- |
1800 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 4 |
44.0 |
MPa |
ASTM D638 |
| 屈服 5 |
45.0 |
MPa |
内部方法 |
| 屈服 6 |
47.0 |
MPa |
ASTM D638 |
| 屈服 |
44.0 |
MPa |
ISO 527-2/5 |
| 屈服 |
47.0 |
MPa |
ISO 527-2/50 |
| 断裂 7 |
50.0 |
MPa |
ASTM D638 |
| 断裂 8 |
47.0 |
MPa |
内部方法 |
| 断裂 9 |
48.0 |
MPa |
ASTM D638 |
| 断裂 |
43.0 |
MPa |
ISO 527-2/5, ISO 527-2/50 |
| 伸长率 |
|
|
|
| 屈服 10 |
4.6 |
% |
ASTM D638 |
| 屈服 11 |
4.6 |
% |
内部方法 |
| 屈服 12 |
4.0 |
% |
ASTM D638 |
| 屈服 |
4.1 |
% |
ISO 527-2/5 |
| 屈服 |
4.6 |
% |
ISO 527-2/50 |
| 断裂 13 |
120 |
% |
ASTM D638 |
| 断裂 14 |
110 |
% |
内部方法 |
| 断裂 15 |
120 |
% |
ASTM D638 |
| 断裂 |
110 |
% |
ISO 527-2/5 |
| 断裂 |
120 |
% |
ISO 527-2/50 |
| 弯曲模量 |
|
|
|
| 50.0 mm 跨距 16 |
1660 |
MPa |
ASTM D790 |
| -- 17 |
1870 |
MPa |
ISO 178 |
| 弯曲应力 |
|
|
|
| -- |
71.0 |
MPa |
ISO 178 |
| 屈服, 50.0 mm 跨距 18 |
70.0 |
MPa |
ASTM D790 |
| 断裂, 50.0 mm 跨距 19 |
69.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 20 |
|
|
ISO 179/1eA |
| -30°C |
48 |
kJ/m² |
ISO 179/1eA |
| 23°C |
56 |
kJ/m² |
ISO 179/1eA |
| 悬壁梁缺口冲击强度 |
|
|
|
| -40°C |
600 |
J/m |
ASTM D256 |
| -30°C |
650 |
J/m |
ASTM D256 |
| -20°C |
700 |
J/m |
ASTM D256 |
| -10°C |
660 |
J/m |
ASTM D256 |
| 0°C |
690 |
J/m |
ASTM D256 |
| 23°C |
720 |
J/m |
ASTM D256 |
| -40°C 21 |
46 |
kJ/m² |
ISO 180/1A |
| -30°C 22 |
48 |
kJ/m² |
ISO 180/1A |
| -20°C 23 |
50 |
kJ/m² |
ISO 180/1A |
| -10°C 24 |
52 |
kJ/m² |
ISO 180/1A |
| 0°C 25 |
55 |
kJ/m² |
ISO 180/1A |
| 23°C 26 |
56 |
kJ/m² |
ISO 180/1A |
| 装有测量仪表的落镖冲击 |
|
|
ASTM D3763 |
| -40°C, Energy at Peak Load |
49.5 |
J |
ASTM D3763 |
| -40°C, Total Energy |
59.2 |
J |
ASTM D3763 |
| -30°C, Energy at Peak Load |
49.5 |
J |
ASTM D3763 |
| -30°C, Total Energy |
61.9 |
J |
ASTM D3763 |
| -20°C, Energy at Peak Load |
41.9 |
J |
ASTM D3763 |
| -20°C, Total Energy |
53.2 |
J |
ASTM D3763 |
| 23°C, Energy at Peak Load |
44.8 |
J |
ASTM D3763 |
| 23°C, Total Energy |
54.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm |
108 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm |
117 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距 27 |
110 |
°C |
ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm |
83.5 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm |
95.9 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 28 |
87.0 |
°C |
ISO 75-2/Af |
| 维卡软化温度 |
|
|
|
| -- |
120 |
°C |
ASTM D1525, ISO 306/B50 15 29 |
| -- |
122 |
°C |
ISO 306/B120 |
| 线形热膨胀系数 |
|
|
|
| 流动 : -40 到 95°C |
9.8E-5 |
cm/cm/°C |
ASTM E831 |
| 流动 : -30 到 80°C |
9.8E-5 |
cm/cm/°C |
ISO 11359-2 |
| 横向 : -40 到 95°C |
1.0E-4 |
cm/cm/°C |
ASTM E831 |
| 横向 : -30 到 80°C |
1.0E-4 |
cm/cm/°C |
ISO 11359-2 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
110 |
°C |
|
| 干燥时间 |
4.0 到 6.0 |
hr |
|
| 干燥时间，*大 |
8.0 |
hr |
|
| 建议的*大水分含量 |
0.020 |
% |
|
| 建议注射量 |
50 到 80 |
% |
|
| 料筒后部温度 |
243 到 266 |
°C |
|
| 料筒中部温度 |
249 到 271 |
°C |
|
| 料筒前部温度 |
254 到 277 |
°C |
|
| 射嘴温度 |
254 到 271 |
°C |
|
| 加工（熔体）温度 |
260 到 277 |
°C |
|
| 模具温度 |
65.6 到 87.8 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
50 到 80 |
rpm |
|
| 排气孔深度 |
0.013 到 0.020 |
mm |
|
| 备注 |
| 1 . |
5.0 mm/min |
| 2 . |
10 mm/min |
| 3 . |
50 mm/min |
| 4 . |
类型 1, 5.0 mm/min |
| 5 . |
类型 1, 10 mm/min |
| 6 . |
类型 1, 50 mm/min |
| 7 . |
类型 1, 5.0 mm/min |
| 8 . |
类型 1, 10 mm/min |
| 9 . |
类型 1, 50 mm/min |
| 10 . |
类型 1, 5.0 mm/min |
| 11 . |
类型 1, 10 mm/min |
| 12 . |
类型 1, 50 mm/min |
| 13 . |
类型 1, 5.0 mm/min |
| 14 . |
类型 1, 10 mm/min |
| 15 . |
类型 1, 50 mm/min |
| 16 . |
1.3 mm/min |
| 17 . |
2.0 mm/min |
| 18 . |
1.3 mm/min |
| 19 . |
1.3 mm/min |
| 20 . |
80*10*4 sp=62mm |
| 21 . |
80*10*4 |
| 22 . |
80*10*4 |
| 23 . |
80*10*4 |
| 24 . |
80*10*4 |
| 25 . |
80*10*4 |
| 26 . |
80*10*4 |
| 27 . |
80*10*4 mm |
| 28 . |
80*10*4 mm |
| 29 . |
标准 B (120°C/h), 载荷2 (50N) |
XENOY材质是什么:
SABIC XENOY塑料PC/PBT/PET树脂是由聚对苯二甲酸丁二酯（PBT）与聚碳酸酯（PC）组成的多能合金塑料共混物。此产品系列具有良好的耐化学剂性和耐热性、即使是低温的情况下，也有极佳的抗冲击性、耐高温、卓越的美感和流动特性。XENOY树脂还有优良的抗紫外性和保色性。
SABIC XENOY树脂系列产品提供良好的耐化学性，在低温，耐热性和出色的审美和流动特性的影响很大阻力，甚至。XENOY合金提供暴露在恶劣的条件下应用的突出表现，或需要高度的韧性。从薄壁汽车减振器和车身壁板，到商业机器的外壳、割草机平台、移动电话等一系列应用。