| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 密度 | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| 水分吸收 | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.50 % | 0.50 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| 熔体流动速率 | 21 g/10 min @Load 2.16 kg, Temperature 265 °C |
21 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| 44 g/10 min @Load 1.20 kg, Temperature 300 °C |
44 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
20 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 150 % | 150 % | Type I, 50 mm/min; ASTM D638 |
| >= 150 % | >= 150 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 1.84 GPa | 267 ksi | 50 mm/min; ASTM D638 |
| 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
| 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 1.94 GPa | 281 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 6.60 J/cm | 12.4 ft-lb/in | ASTM D256 |
| 0.560 J/cm @Temperature -30.0 °C |
1.05 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature -10.0 °C |
2.38 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 落锤总能量 | 95.0 J @Temperature 23.0 °C |
70.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 线性热膨胀系数,横向流动 | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| 载荷下热变形温度(0.46 MPa) | 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 维卡软化温度 | 106 °C | 223 °F | Rate B/120; ISO 306 |
| 107 °C | 225 °F | Rate B/50; ISO 306 | |
| 108 °C | 226 °F | Rate B/50; ASTM D1525 | |
| 可燃性(UL94) | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 雾度 | 2.0 % @Thickness 2.54 mm |
2.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
PC/PET合金材料介绍
PC/PET合金材料由PC(聚碳酸酷)和PET(聚对苯二甲酸乙二酷)共混造料聚合而成。通常以共混造料后，以粒料形状供应。如果只把两种料简单的混合后，直接注塑，效果很差，会出现分层现象。
PC 全名是聚碳酸醋，是分子链中含有碳酸酷基的高分子聚合物，根据酷基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。PC 的优点是室温刚而韧但高温的情况下，热变形严重。缺点是应力开裂，粘度大，易粘模。
PET树脂英文名称:Polybutylene Terephthalate Resin。它由(DMT)进行酷交换或与精对苯二甲由1.4丁二醇与对苯二甲酸二甲酷酸(PTA)直接酷化后再经缩聚制得。其分子式为:(-C12H804-)nPET树脂为结晶形，熔点225C左右，相对密度 1.32:具有优良的力学性能，有自润滑性和耐磨性，摩擦系数低，耐热、耐候好:但缺口敏感性大:尺寸稳定性好，电性能优良，耐电弧性好:抗化学性及其优异，与醇、醚、脂肪烃、酸和盐的水溶液等不起作用，但不耐强酸和强藏。耐四氯化碳,在二氯乙烷中溶胀，在芳烃、乙酸中有些溶胀。
PC/PET合金艰巨了两款材料的优点，具有良好的硬度和耐冲击、高透光率、高光泽、高韧性(即使在低温环境中)、良好的耐化学品性，也改善了缺点，不易发生应力开裂，良好的涂覆性能，低吸湿率，易脱模。
PC/PET的特性:
(1)一般性能 PET树脂为乳白色半透明或无色透明体，相对密度1.38，透光率为90%。PET属于中等阻隔性材料。PET的吸水率为0.6%，吸水性较大。
(2)力学性能PET膜的拉伸强度很高，可与铝箔婚美，是HDPE膜的9倍，是PC和PA膜的3倍。增强PET的端小、耐疲劳极好(好于增强PC和PA)、耐磨性和耐摩擦性良好。PET的力学性能受温度影响较小。
(3)热学性能 纯PET 的耐热性能不高，但增强处理后大幅度提高，在180C时的机械性能比PF层压板好，是增强的热塑性工程塑料中耐热较好的品种。PET的耐热老化性好，脆化温度为-70C，在-30C时仍具有一定韧性。PET不易燃烧，火焰呈黄色，有滴落。
(4)电学性能 PET虽为极性聚合物，但电绝缘性优良，在高频下仍能很好保持PET的耐电晕性较差，不能用于高压绝缘:电绝缘性受温度和湿度影响，并以湿度的影响较大
PC/PET 的应用:
有优异的性能，被广泛的用于密封材料、滑动材料、防腐材料、绝缘材料及医用材料等。具体有:
(1)耐腐蚀方面用纯F4树脂制造各种化工容器和零件，如管材、储罐、反应釜、设备衬里、阀门、泵体、接头、过滤材料、分离材料等一切与有腐蚀性介质接触的制品。
(2)耐磨方面对F4进行填充耐磨改性处理，可用于耐磨材料，如转动、静密封环、活塞环、垫圈、阀瓣、阀座、轴承、轴瓦、滑块、导轨等
(3)绝缘材料用纯F4树脂制造耐高温、高频电绝缘制品，如高频绝缘子、高频电缆、耐潮湿电缆、电容器线圈、电机槽的绝缘及集成电路板等。
沙伯基础PC/PET型号介绍:
XYLEXMRESINSHX7509HP
XYLEXM RESINSHX8300HP
XYLEXM RESINSX7300
XYLEXM RESINSX7300CLX7607XYLEXD RESINS
XYLEXmRESINSX7519HP
XYLEXNRESINSX8210
XYLEXM RESINSX8300
XYLEXM RESINSX84109ACXYLEXMRESINS
X8519
| 厂家： | 基础创新塑料美国 |
| 加工级别： | 挤出 |
| 特性： | 阻燃;抗紫外;耐高温 |
| 是否环保： | 是 |
| 颜色： | 本色 |
| 用途： | 专用粒料 |
| 品牌： | 基础创新塑料美国 |
| 型号： | X7300CL NA9A002 |