1

SABIC Innovative Plastics Lexan® HPS4 PC

Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable. Contains mold release.

 

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.19 g/cc	1.19 g/cc	ASTM D792
密度	1.19 g/cc	0.0430 lb/in³	ISO 1183
吸水率	0.14 % @Time 86400 sec	0.14 % @Time 24.0 hour	ASTM D570
水分吸收	0.100 %	0.100 %	23°C / 50% RH; ISO 62
饱和吸水率	0.26 %	0.26 %	ISO 62
线性成型收缩率,Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on Tensile Bar; SABIC Method
	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
线性成型收缩率，横向	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	10.5 g/10 min @Load 1.20 kg, Temperature 300 °C	10.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
化合物熔体指数	10 g/10 min @Load 1.20 kg, Temperature 300 °C	10 g/10 min @Load 2.65 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	73.0 MPa	10600 psi	50 mm/min; ISO 527
	74.0 MPa	10700 psi	Type I, 50 mm/min; ASTM D638
抗张强度(屈服)	61.0 MPa	8850 psi	50 mm/min; ISO 527
	62.0 MPa	8990 psi	Type I, 50 mm/min; ASTM D638
伸长率 (断裂)	128 %	128 %	50 mm/min; ISO 527
	140 %	140 %	Type I, 50 mm/min; ASTM D638
屈服伸长率	6.0 %	6.0 %	50 mm/min; ISO 527
	6.5 %	6.5 %	Type I, 50 mm/min; ASTM D638
拉伸模量	2.30 GPa	334 ksi	50 mm/min; ASTM D638
	2.39 GPa	347 ksi	1 mm/min; ISO 527
弯曲强度	93.0 MPa	13500 psi	2 mm/min; ISO 178
	100 MPa	14500 psi	1.3 mm/min, 50 mm span; ASTM D790
弯曲模量	2.25 GPa	326 ksi	2 mm/min; ISO 178
	2.40 GPa	348 ksi	1.3 mm/min, 50 mm span; ASTM D790
悬壁梁缺口冲击强度	8.40 J/cm	15.7 ft-lb/in	ASTM D256
	2.20 J/cm @Temperature -30.0 °C	4.12 ft-lb/in @Temperature -22.0 °F	ASTM D256
	70.0 kJ/m²	33.3 ft-lb/in²	80*10*3; ISO 180/1A
	10.0 kJ/m² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	80*10*3; ISO 180/1A
悬壁梁无缺口冲击强度	NB	NB	80*10*3; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80*10*3; ISO 180/1U
简支梁无缺口冲击强度	NB	NB	Edgew 80*10*3 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eU
简支梁缺口冲击强度	7.00 J/cm²	33.3 ft-lb/in²	Edgew 80*10*3 sp=62mm; ISO 179/1eA
	8.20 J/cm²	39.0 ft-lb/in²	ISO 179/2C
	1.50 J/cm² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eA
落锤总能量	88.0 J @Temperature 23.0 °C	64.9 ft-lb @Temperature 73.4 °F	ASTM D3763

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	78.0 µm/m-°C @Temperature -40.0 - 40.0 °C	43.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	78.0 µm/m-°C @Temperature -40.0 - 40.0 °C	43.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
线性热膨胀系数,横向流动	76.0 µm/m-°C @Temperature -40.0 - 40.0 °C	42.2 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	76.0 µm/m-°C @Temperature -40.0 - 40.0 °C	42.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
载荷下热变形温度(0.46 MPa)	138 °C @Thickness 6.40 mm	280 °F @Thickness 0.252 in	unannealed; ASTM D648
载荷下热变形温度(1.8 MPa)	127 °C	261 °F	Edgew 120*10*4 sp=100mm; ISO 75/Ae
	126 °C @Thickness 3.20 mm	259 °F @Thickness 0.126 in	unannealed; ASTM D648
	132 °C @Thickness 6.40 mm	270 °F @Thickness 0.252 in	unannealed; ASTM D648
维卡软化温度	143 °C	289 °F	Rate B/50; ASTM D1525
	143 °C	289 °F	Rate B/50; ISO 306
	145 °C	293 °F	Rate B/120; ISO 306

材料描述		测试方法
球压试验，125°C+/-2℃	PASSES	IEC 60695-10-2

代理无卤阻燃高透明PC料,普通阻燃高透明PC料,加纤阻燃PC料,超韧耐寒PC料,扩散PC料,遮光PC料等等.

聚碳酸酯（Polycarbonate）缩写为PC, 俗称防弹胶，是一种无色透明的无定性热塑性材料。

PC化学性质:聚碳酸酯耐酸，耐油，不耐强碱。PC物理性质:聚碳酸酯无色透明，耐热，抗冲击，阻燃，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大，聚碳酸酯同聚甲基丙烯酸甲酯之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。

PC优点：1、具高强度及弹性系数、高冲击强度、使用温度范围广；

2、高度透明性及自由染色性；

3、H.D.T.高；

4、耐疲劳性佳；

5、耐候性佳；

6、电气特性优；

7、无味无臭对人体无害符合卫生安全；

8、成形收缩率低、尺寸安定性良好。

PC用途：1、电子电器：CD片、开关、家电外壳、信号筒、电容器、电话机壳体、电话交换器、信号继电器及零件等；2、汽车：保险杆、分电盘、安全玻璃等；3、工业零件：照相机本体、机具外壳、安全帽、潜水镜、安全镜片等；4、光学照明：大型灯罩、防护玻璃、光学仪器的左右目镜筒等；5、高精度零件：电子计算机、视频录象机等；6、机械设备：各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮、机械设备壳体、罩盖及框架等；7、医疗器材：医用杯、筒、瓶、牙科器械、药品容器和手术器械，还可用作人工肾、人工肺等人工脏器；8、其它方面：建筑上用作中空筋双壁板、暖房玻璃等；纺织行业用作纺织纱管、纺织机轴瓦等；日用方面用作奶瓶、餐具、玩具、模型、绝缘接插件、线圈框架、管座、绝缘套管、矿灯的电池壳、绝缘皮包、录音带、彩色录象磁带等。

PC分类：防静电PC、导电PC、加纤防火PC、抗紫外线耐候PC、食品级PC

 

长期供应：光扩散PC,导电PC,透明无卤阻燃PC,玻纤增强PC,高耐热PC,吹塑级PC,食品级PC,医疗级PC,挤出级PC,光学级PC,低温耐冲击PC,无氯无溴阻燃PC,抗静电PC. PC阻燃级 PCSAE适合级 PC镜片级 PC耐γ线级 PC光扩散级 PC光反射级 PC導光板级 PC一般玻纤强化级 PC高流动玻纤强化级 PC低各向异性玻纤强化级 PC 高阻燃玻纤强化级 PC复合强化低翘曲级 PC复合强化低翘曲阻燃级 PC相机用玻纤强化级 PC手机外壳级 PC非溴非磷阻燃强化级 PC非溴非磷阻燃玻纤强化高流动级 PC非溴非磷阻燃玻纤强化级（照相机用） PC非溴非磷阻燃复合强化低翘曲级 PC非溴非磷阻燃低各向异性玻纤强化级 PC炭纤强化级 PC炭纤 玻纤强化级 PC耐磨性改良级 PC非溴非磷阻燃炭纤强化级 PC耐磨性改良 强化级-1 PC耐磨性改良 强化级-2