SABIC Innovative Plastics Lexan® HPS7 PC

Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. Contains mold release.

 

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.20 g/cc	1.20 g/cc	ASTM D792
密度	1.19 g/cc	0.0430 lb/in³	ISO 1183
吸水率	0.14 % @Time 86400 sec	0.14 % @Time 24.0 hour	ASTM D570
水分吸收	0.100 %	0.100 %	23°C / 50% RH; ISO 62
饱和吸水率	0.26 %	0.26 %	ISO 62
线性成型收缩率,Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on Tensile Bar; SABIC Method
	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
线性成型收缩率，横向	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	5.0 g/10 min @Load 1.20 kg, Temperature 300 °C	5.0 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
	24 g/10 min @Load 5.00 kg, Temperature 300 °C	24 g/10 min @Load 11.0 lb, Temperature 572 °F	ASTM D1238
化合物熔体指数	5.0 g/10 min @Load 1.20 kg, Temperature 300 °C	5.0 g/10 min @Load 2.65 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	71.0 MPa	10300 psi	50 mm/min; ISO 527
	72.0 MPa	10400 psi	Type I, 50 mm/min; ASTM D638
抗张强度(屈服)	61.0 MPa	8850 psi	50 mm/min; ISO 527
	62.0 MPa	8990 psi	Type I, 50 mm/min; ASTM D638
伸长率 (断裂)	125 %	125 %	Type I, 50 mm/min; ASTM D638
	126 %	126 %	50 mm/min; ISO 527
屈服伸长率	5.9 %	5.9 %	50 mm/min; ISO 527
	6.5 %	6.5 %	Type I, 50 mm/min; ASTM D638
拉伸模量	2.27 GPa	329 ksi	50 mm/min; ASTM D638
	2.45 GPa	355 ksi	1 mm/min; ISO 527
弯曲强度	95.0 MPa	13800 psi	2 mm/min; ISO 178
	100 MPa	14500 psi	1.3 mm/min, 50 mm span; ASTM D790
弯曲模量	2.20 GPa	319 ksi	2 mm/min; ISO 178
	2.34 GPa	339 ksi	1.3 mm/min, 50 mm span; ASTM D790
悬壁梁缺口冲击强度	9.35 J/cm	17.5 ft-lb/in	ASTM D256
	7.85 J/cm @Temperature -30.0 °C	14.7 ft-lb/in @Temperature -22.0 °F	ASTM D256
悬壁梁无缺口冲击强度	27.0 J/cm	50.6 ft-lb/in	ASTM D4812
悬壁梁缺口冲击强度	75.0 kJ/m²	35.7 ft-lb/in²	80*10*3; ISO 180/1A
	15.0 kJ/m² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	80*10*3; ISO 180/1A
悬壁梁无缺口冲击强度	NB	NB	80*10*3; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80*10*3; ISO 180/1U
简支梁无缺口冲击强度	NB	NB	Edgew 80*10*3 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eU
简支梁缺口冲击强度	7.50 J/cm²	35.7 ft-lb/in²	Edgew 80*10*3 sp=62mm; ISO 179/1eA
	1.50 J/cm² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eA
落锤总能量	82.0 J @Temperature 23.0 °C	60.5 ft-lb @Temperature 73.4 °F	ASTM D3763

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	66.0 µm/m-°C @Temperature -40.0 - 40.0 °C	36.7 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	66.0 µm/m-°C @Temperature -40.0 - 40.0 °C	36.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
线性热膨胀系数,横向流动	75.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.7 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	75.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.7 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	141 °C @Thickness 3.20 mm	286 °F @Thickness 0.126 in	unannealed; ASTM D648
	141 °C @Thickness 6.40 mm	286 °F @Thickness 0.252 in	unannealed; ASTM D648
载荷下热变形温度(1.8 MPa)	128 °C	262 °F	Flatw 80*10*4 sp=64mm; ISO 75/Af
	129 °C @Thickness 3.20 mm	264 °F @Thickness 0.126 in	unannealed; ASTM D648
	132 °C @Thickness 6.40 mm	270 °F @Thickness 0.252 in	unannealed; ASTM D648
维卡软化温度	145 °C	293 °F	Rate B/50; ASTM D1525
	145 °C	293 °F	Rate B/50; ISO 306
	146 °C	295 °F	Rate B/120; ISO 306

材料描述		测试方法
Ball Pressure Test, 75°C +/- 2°C	PASSES	IEC 60695-10-2

代理无卤阻燃高透明PC料,普通阻燃高透明PC料,加纤阻燃PC料,超韧耐寒PC料,扩散PC料,遮光PC料等等.

聚碳酸酯（Polycarbonate）缩写为PC, 俗称防弹胶，是一种无色透明的无定性热塑性材料。

PC化学性质:聚碳酸酯耐酸，耐油，不耐强碱。PC物理性质:聚碳酸酯无色透明，耐热，抗冲击，阻燃，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大，聚碳酸酯同聚甲基丙烯酸甲酯之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。

PC优点：1、具高强度及弹性系数、高冲击强度、使用温度范围广；

2、高度透明性及自由染色性；

3、H.D.T.高；

4、耐疲劳性佳；

5、耐候性佳；

6、电气特性优；

7、无味无臭对人体无害符合卫生安全；

8、成形收缩率低、尺寸安定性良好。

PC用途：1、电子电器：CD片、开关、家电外壳、信号筒、电容器、电话机壳体、电话交换器、信号继电器及零件等；2、汽车：保险杆、分电盘、安全玻璃等；3、工业零件：照相机本体、机具外壳、安全帽、潜水镜、安全镜片等；4、光学照明：大型灯罩、防护玻璃、光学仪器的左右目镜筒等；5、高精度零件：电子计算机、视频录象机等；6、机械设备：各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮、机械设备壳体、罩盖及框架等；7、医疗器材：医用杯、筒、瓶、牙科器械、药品容器和手术器械，还可用作人工肾、人工肺等人工脏器；8、其它方面：建筑上用作中空筋双壁板、暖房玻璃等；纺织行业用作纺织纱管、纺织机轴瓦等；日用方面用作奶瓶、餐具、玩具、模型、绝缘接插件、线圈框架、管座、绝缘套管、矿灯的电池壳、绝缘皮包、录音带、彩色录象磁带等。

PC分类：防静电PC、导电PC、加纤防火PC、抗紫外线耐候PC、食品级PC

 

长期供应：光扩散PC,导电PC,透明无卤阻燃PC,玻纤增强PC,高耐热PC,吹塑级PC,食品级PC,医疗级PC,挤出级PC,光学级PC,低温耐冲击PC,无氯无溴阻燃PC,抗静电PC. PC阻燃级 PCSAE适合级 PC镜片级 PC耐γ线级 PC光扩散级 PC光反射级 PC導光板级 PC一般玻纤强化级 PC高流动玻纤强化级 PC低各向异性玻纤强化级 PC 高阻燃玻纤强化级 PC复合强化低翘曲级 PC复合强化低翘曲阻燃级 PC相机用玻纤强化级 PC手机外壳级 PC非溴非磷阻燃强化级 PC非溴非磷阻燃玻纤强化高流动级 PC非溴非磷阻燃玻纤强化级（照相机用） PC非溴非磷阻燃复合强化低翘曲级 PC非溴非磷阻燃低各向异性玻纤强化级 PC炭纤强化级 PC炭纤 玻纤强化级 PC耐磨性改良级 PC非溴非磷阻燃炭纤强化级 PC耐磨性改良 强化级-1 PC耐磨性改良 强化级-2