SABIC Innovative Plastics Lexan® HPH4504 PPC

Polycarbonate, Gamma Radiation Resistant
SABIC Innovative Plastics (GE Plastics)
产品说明：
High heat specialty polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, steam, gamma and e-beam sterilizable.

This data was supplied by SABIC-IP for the Americas region.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.20 g/cc	1.20 g/cc	ASTM D 792
密度	1.19 g/cc	0.0430 lb/in³	ASTM D 792
	1.20 g/cc	0.0434 lb/in³	ISO 1183
吸水率	0.16 % @Time 86400 sec	0.16 % @Time 24.0 hour	ASTM D 570
平衡吸湿	0.35 %	0.35 %	23°C / 50% RH; ISO 62
饱和吸水率	0.16 % @Temperature 23.0 °C	0.16 % @Temperature 73.4 °F	ISO 62
线性成型收缩率,Flow	0.0070 - 0.0080 cm/cm @Thickness 3.20 mm	0.0070 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	3.0 g/10 min @Load 1.20 kg, Temperature 300 °C	3.0 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D 1238
	3.0 g/10 min @Load 1.20 kg, Temperature 300 °C	3.0 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（M 级）	85	85	ASTM D 785
洛氏硬度（R 级）	122	122	ASTM D 785
抗张强度(断裂)	65.0 MPa	9430 psi	50 mm/min; ISO 527
	71.0 MPa	10300 psi	Type I, 50 mm/min; ASTM D 638
抗张强度(屈服)	65.0 MPa	9430 psi	Type I, 50 mm/min; ASTM D 638
	65.0 MPa	9430 psi	50 mm/min; ISO 527
伸长率 (断裂)	7.0 %	7.0 %	50 mm/min; ISO 527
	122 %	122 %	Type I, 50 mm/min; ASTM D 638
屈服伸长率	7.0 %	7.0 %	Type I, 50 mm/min; ASTM D 638
	7.0 %	7.0 %	50 mm/min; ISO 527
拉伸模量	2.09 GPa	303 ksi	5 mm/min; ASTM D 638
	2.26 GPa	328 ksi	1 mm/min; ISO 527
弯曲强度	66.0 MPa	9570 psi	2 mm/min; ISO 178
	95.0 MPa	13800 psi	1.3 mm/min, 50 mm span; ASTM D 790
弯曲模量	2.02 GPa	293 ksi	1.3 mm/min, 50 mm span; ASTM D 790
	2.12 GPa	307 ksi	2 mm/min; ISO 178
悬壁梁缺口冲击强度	1.44 J/cm @Temperature -30.0 °C	2.70 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	6.40 J/cm @Temperature 23.0 °C	12.0 ft-lb/in @Temperature 73.4 °F	ASTM D 256
悬壁梁无缺口冲击强度	32.04 J/cm @Temperature 23.0 °C	60.02 ft-lb/in @Temperature 73.4 °F	ASTM D 4812
悬壁梁缺口冲击强度	11.0 kJ/m² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	80*10*4; ISO 180/1A
	13.0 kJ/m² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	80*10*4; ISO 180/1A
简支梁缺口冲击强度	1.50 J/cm² @Temperature 23.0 °C	7.14 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
拉伸冲击强度	577 kJ/m²	275 ft-lb/in²	Type S; ASTM D 1822
落锤总能量	149 J @Temperature 23.0 °C	110 ft-lb @Temperature 73.4 °F	ASTM D 3029
冲击试验	73.0 J @Temperature 23.0 °C	53.8 ft-lb @Temperature 73.4 °F	Instrumented Impact Total Energy; ASTM D 3763

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= 2.60e+17 ohm-cm	>= 2.60e+17 ohm-cm	ASTM D 257
介电常数	3.0 @Frequency 1.00e+6 Hz	3.0 @Frequency 1.00e+6 Hz	ASTM D 150
	3.15 @Frequency 50.0 - 60.0 Hz	3.15 @Frequency 50.0 - 60.0 Hz	ASTM D 150
介电强度	20.2 kV/mm @Thickness 3.20 mm	513 kV/in @Thickness 0.126 in	in air; ASTM D 149
耗散因数	0.0012 @Frequency 50.0 - 60.0 Hz	0.0012 @Frequency 50.0 - 60.0 Hz	ASTM D 150
	0.024 @Frequency 100 Hz	0.024 @Frequency 100 Hz	ASTM D 150
相比耐漏电起痕指数(CTI)	175 - 250 V	175 - 250 V	PLC code 3; UL 746A
热丝引燃 (HWI)	30 - 60 sec	30 - 60 sec	PLC code 2; UL 746A
高电弧燃烧，HAI	0.00 - 15 arcs	0.00 - 15 arcs	surface, PLC code 4; UL 746A
高压电弧跟踪率，HVTR	80.0 - 150 mm/min	3.15 - 5.91 in/min	PLC code 3; UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	91.8 µm/m-°C @Temperature -40.0 - 95.0 °C	51.0 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
线性热膨胀系数,横向流动	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
比热容	1.25 J/g-°C	0.299 BTU/lb-°F	ASTM C 351
导热系数	0.210 W/m-K	1.46 BTU-in/hr-ft²-°F	ASTM C 177
载荷下热变形温度(1.8 MPa)	132 °C	270 °F	Flatw 80*10*4 sp=64mm; ISO 75/Af
	143 °C @Thickness 3.20 mm	289 °F @Thickness 0.126 in	unannealed; ASTM D 648
维卡软化温度	154 °C	309 °F	Rate B/50; ISO 306
	155 °C	311 °F	Rate B/120; ISO 306
	160 °C	320 °F	Rate B/50; ASTM D 1525
UL RTI	125 °C	257 °F	UL 746B
UL RTI，机械冲击	125 °C	257 °F	UL 746B
UL RTI，机械无冲击	125 °C	257 °F	UL 746B

光学性能	额定值 (公制)	额定值 (英制)	测试方法
折射率	1.60	1.60	ASTM D 542
雾度	1.0 % @Thickness 2.54 mm	1.0 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible	85 % @Thickness 2.54 mm	85 % @Thickness 0.100 in	ASTM D 1003

代理无卤阻燃高透明PC料,普通阻燃高透明PC料,加纤阻燃PC料,超韧耐寒PC料,扩散PC料,遮光PC料等等.

聚碳酸酯（Polycarbonate）缩写为PC, 俗称防弹胶，是一种无色透明的无定性热塑性材料。

PC化学性质:聚碳酸酯耐酸，耐油，不耐强碱。PC物理性质:聚碳酸酯无色透明，耐热，抗冲击，阻燃，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大，聚碳酸酯同聚甲基丙烯酸甲酯之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。

PC优点：1、具高强度及弹性系数、高冲击强度、使用温度范围广；

2、高度透明性及自由染色性；

3、H.D.T.高；

4、耐疲劳性佳；

5、耐候性佳；

6、电气特性优；

7、无味无臭对人体无害符合卫生安全；

8、成形收缩率低、尺寸安定性良好。

PC用途：1、电子电器：CD片、开关、家电外壳、信号筒、电容器、电话机壳体、电话交换器、信号继电器及零件等；2、汽车：保险杆、分电盘、安全玻璃等；3、工业零件：照相机本体、机具外壳、安全帽、潜水镜、安全镜片等；4、光学照明：大型灯罩、防护玻璃、光学仪器的左右目镜筒等；5、高精度零件：电子计算机、视频录象机等；6、机械设备：各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮、机械设备壳体、罩盖及框架等；7、医疗器材：医用杯、筒、瓶、牙科器械、药品容器和手术器械，还可用作人工肾、人工肺等人工脏器；8、其它方面：建筑上用作中空筋双壁板、暖房玻璃等；纺织行业用作纺织纱管、纺织机轴瓦等；日用方面用作奶瓶、餐具、玩具、模型、绝缘接插件、线圈框架、管座、绝缘套管、矿灯的电池壳、绝缘皮包、录音带、彩色录象磁带等。

PC分类：防静电PC、导电PC、加纤防火PC、抗紫外线耐候PC、食品级PC

 

长期供应：光扩散PC,导电PC,透明无卤阻燃PC,玻纤增强PC,高耐热PC,吹塑级PC,食品级PC,医疗级PC,挤出级PC,光学级PC,低温耐冲击PC,无氯无溴阻燃PC,抗静电PC. PC阻燃级 PCSAE适合级 PC镜片级 PC耐γ线级 PC光扩散级 PC光反射级 PC導光板级 PC一般玻纤强化级 PC高流动玻纤强化级 PC低各向异性玻纤强化级 PC 高阻燃玻纤强化级 PC复合强化低翘曲级 PC复合强化低翘曲阻燃级 PC相机用玻纤强化级 PC手机外壳级 PC非溴非磷阻燃强化级 PC非溴非磷阻燃玻纤强化高流动级 PC非溴非磷阻燃玻纤强化级（照相机用） PC非溴非磷阻燃复合强化低翘曲级 PC非溴非磷阻燃低各向异性玻纤强化级 PC炭纤强化级 PC炭纤 玻纤强化级 PC耐磨性改良级 PC非溴非磷阻燃炭纤强化级 PC耐磨性改良 强化级-1 PC耐磨性改良 强化级-2