Topas Advanced Polymers TOPAS® 8007X10 Cyclic Olefin Copolymer (COC)

Cyclo Olefin Polymer
Topas Advanced Polymers
产品说明：
TOPAS® 8007X10 is a highly UV-transparent version of our 8007 series of injection molding resins. Like the rest of the 8007 grades, 8007X10 is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for diagnostic and analytical products. It transmits ultraviolet light at lower wavelengths than other polymers. Analytical results are more accurate with pure TOPAS COC and its higher UV transmission for more precise analysis in contact with sensitive chemistries.

Key applications and attributes:

• Cuvettes: UV transparency at low wavelengths
• Microplates and biochips: Dimensional stability and purity and chemical resistance
• Microfluidics: UV transmission; exceptional mold detail replication
• Optics: Clarity, low birefringence, low fluorescence
• High purity applications: Not manufactured with BPA, phthalates, or halogens

Information provided by TOPAS Advanced Polymers

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.02 g/cc	0.0368 lb/in³	ISO 1183
饱和吸水率	0.010 % @Temperature 23.0 °C	0.010 % @Temperature 73.4 °F	ISO 62
熔体流动速率	29.4 g/10 min @Load 2.16 kg, Temperature 260 °C	29.4 g/10 min @Load 4.76 lb, Temperature 500 °F	ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(屈服)	63.0 MPa	9140 psi	50mm/min; ISO 527-2/1A
屈服伸长率	4.5 %	4.5 %	50mm/min; ISO 527-2/1A
拉伸模量	2.60 GPa	377 ksi	1mm/min; ISO 527-2/1A
简支梁无缺口冲击强度	2.00 J/cm² @Temperature 23.0 °C	9.52 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
简支梁缺口冲击强度	0.260 J/cm² @Temperature 23.0 °C	1.24 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
介电常数	2.35 @Frequency 1000 - 10000 Hz	2.35 @Frequency 1000 - 10000 Hz	IEC 60250
相比耐漏电起痕指数(CTI)	>= 600 V	>= 600 V	IEC 60112

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(0.46 MPa)	75.0 °C	167 °F	ISO 75-1,-2
维卡软化温度	80.0 °C	176 °F	B50 (50°C/h 50N); ISO 306
玻璃化转变温度，Tg	78.0 °C	172 °F	10°C/min; ISO 11357-1,-2,-3
可燃性(UL94)	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

光学性能	额定值 (公制)	额定值 (英制)	测试方法
折射率	1.53	1.53	ISO 489
Transmission, Visible	91 %	91 %	ISO 13468-2

加工性能	额定值 (公制)	额定值 (英制)	测试方法
进料温度	<= 60.0 °C	<= 140 °F
射嘴温度	220 - 250 °C	428 - 482 °F
1区	190 - 220 °C	374 - 428 °F
2区	200 - 230 °C	392 - 446 °F
3区	210 - 240 °C	410 - 464 °F
4区	220 - 250 °C	428 - 482 °F
模具温度	40.0 - 70.0 °C	104 - 158 °F
射速	50.0 - 150 mm/sec	1.97 - 5.91 in/sec	Moderate to Fast
注射压力	50.0 - 110 MPa	7250 - 16000 psi	Specific
保压	30.0 - 60.0 MPa	4350 - 8700 psi	Specific
背压	<= 15.0 MPa	<= 2180 psi	Specific
螺杆转速	50 - 200 rpm	50 - 200 rpm

COC性能特点：

1、耐.磨性：耐.磨性（跟分子量成正比）居塑料之冠，并超过某些金属（砂浆磨耗测试装置）

2、耐冲击性：分子量达到150万时 值；

3、自润滑性：摩擦系数0.05～0.11，在水为润滑剂的情况下为PA6的1/2；在无润滑剂的情况下仅次于PTFE；

4、耐化学药品性：20℃～80℃能耐80多种溶剂，而且无任何反常现象；

5、冲击能吸收性：冲击能吸收值在所有塑料中 ，因而噪声阻尼性很好；

6、极低的饱和吸水率：0.01% 7、超低温使用：能在-80℃的环境下长期使用 UHMW-PE是一种另人惊异的工程塑料。具有可与聚四氟乙烯（PTFE）相匹敌

 

TOPAS? 8007X10

环烯烃共聚物

Topas Advanced Polymers, Inc.

产品说明 TOPAS 8007X10 是我们的 8007 系列注塑成型树脂的高度紫外线透明版本。与其他 8007 等级一样，8007X10 是一种透明无定形聚合物，具有出色的防潮性、耐化学性、高纯度和非反应性表面，使其成为诊断和分析产品的绝佳选择。它比其他聚合物传输更低波长的紫外线。纯 TOPAS COC 的分析结果更准确，其更高的紫外线透射率可在接触敏感化学品时进行更精确的分析。选定的应用 比色皿 微孔板 生物芯片 微流体 光学 高纯度应用 医疗保健和食品接触

领先的属性 低波长下的紫外线透明度 具有紫外线透射的尺寸稳定性 纯度和耐化学性 出色的模具细节复制；可加工 清晰度、低双折射、低荧光 不使用 BPA、邻苯二甲酸盐或卤素制造 广泛的法规遵从性 用于注塑成型、医疗保健、光学和诊断的相关等级 TOPAS 8007S-04 - 标准等级，适用于大多数应用 TOPAS 8007D-61 - 外部润滑8007S-04 用于瓶子、小瓶等的吹塑成型。